{"schema_version":"1.0","canonical_url":"https://patentable.app/patents/US-11512364","patent":{"patent_number":"US-11512364","title":"Method for producing a hot strip of a bainitic multi-phase steel having a Zn—Mg—Al coating, and a corresponding hot strip","assignee":null,"inventors":[],"filing_date":"2020-07-28T00:00:00.000Z","publication_date":"2022-11-29T00:00:00.000Z","cpc_codes":["G06V","G06V","G09G","G09G","G09G"],"num_claims":14,"abstract":"The invention relates to a method for producing a hot-rolled strip composed of a bainitic multi-phase steel and having a Zn—Mg—Al coating, comprising the following steps: melting a steel melt containing (in weight percent): C: 0.04-0.11, Si: <=0.7, Mn: 1.4-2.2, Mo: 0.05-0.5, Al: 0.015-0.1, P: up to 0.02, S: up to 0.01, B: up to 0.006, and at least one element from the group Nb, V, Ti in accordance with the following condition: 0.02<=Nb+V+Ti<=0.20, the remainder being iron including unavoidable steel-accompanying elements resulting from the melting process, casting the steel melt into a preliminary material, in particular a slab or a block or a thin slab, hot rolling the preliminary material into a hot-rolled strip having a final rolling temperature in the range of 800 to 950° C., cooling the hot-rolled strip to a winding temperature less than 650° C., winding the hot-rolled strip at a winding temperature less than 650° C., cooling the wound hot-rolled strip to room temperature in still air, wherein the microstructure of the wound hot-rolled strip then has a bainite fraction greater than 50% after the hot rolling, heating the hot-rolled strip to a temperature greater than 650° C. and less than Ac3, in particular less than Ac1+50° C., cooling the hot-rolled strip to zinc bath temperature, hot-dip coating the heated hot-rolled strip in a zinc alloy molten bath containing (in weight percent): Al: 1.0-2.0, Mg: 1.0-2.0, the remainder being zinc and unavoidable impurities. The invention further relates to the hot-rolled strip produced in accordance with the method above and to shaped, dynamically highly loadable components, in particular motor vehicle parts, that are produced from said hot-roiled strip and that are resistant to corrosive and abrasive influences."},"analysis":{"summary":null,"layman_explanation":null,"technical_analysis":null,"business_analysis":null,"faqs":null,"topics":[],"tech_cluster":null},"seo":{"title":"Method for producing a hot strip of a bainitic multi-phase steel having a Zn—Mg—Al coating, and a corresponding hot strip","description":"The invention relates to a method for producing a hot-rolled strip composed of a bainitic multi-phase steel and having a Zn—Mg—Al coating, comprising the following steps: melting a steel melt containi","keywords":[]},"attribution":{"source":"Patentable","source_url":"https://patentable.app","canonical_url":"https://patentable.app/patents/US-11512364","license":"CC-BY-4.0-like","license_terms":"AI-generated analysis on this page (summary, layman_explanation, technical_analysis, business_analysis, faqs) may be reused with attribution and a visible link back to the canonical URL above. Patent abstracts, claims, and bibliographic data are USPTO public domain.","required_link":"https://patentable.app/patents/US-11512364","citation_suggestion":"Patentable. \"Method for producing a hot strip of a bainitic multi-phase steel having a Zn—Mg—Al coating, and a corresponding hot strip\" (US-11512364). https://patentable.app/patents/US-11512364","copyright_holder":"Nomic Interactive Technology LLC"},"links":{"html":"https://patentable.app/patents/US-11512364","json":"https://patentable.app/api/llm-context/US-11512364","site":"https://patentable.app","llms_txt":"https://patentable.app/llms.txt"},"generated_at":"2026-05-31T05:13:38.392Z"}